Sinterigita NdFeB-Magneto
| Sinterigitaj NdFeB-Magnetaj Fizikaj Posedaĵoj | ||||||||
| Grado | Remanence | Pastro Temp.- Coeff. De Br | Truda Forto | Interna Truda Forto | Pastro Temp.- Coeff. De Hcj | Maks. Energia Produkto | Maks. Funkcianta Temperaturo | Denseco |
| Br (KGs) | Hcb (KOe) | Hcj (KOe) | (BH) maks. (MGOe) | g / cm³ | ||||
| N35 | 11.7-12.2 | -0.11 ~ -0.12 | ≥10.9 | ≥12 | -0.58 ~ -0.78 | 33-36 | 80 ℃ | 7.6 |
| N38 | 12.2-12.5 | -0.11 ~ -0.12 | ≥11.3 | ≥12 | -0.58 ~ -0.78 | 36-39 | 80 ℃ | 7.6 |
| N40 | 12.5-12.8 | -0.11 ~ -0.12 | ≥11,5 | ≥12 | -0.58 ~ -0.78 | 38-41 | 80 ℃ | 7.6 |
| N42 | 12.8-13.2 | -0.11 ~ -0.12 | ≥11,5 | ≥12 | -0.58 ~ -0.78 | 40-43 | 80 ℃ | 7.6 |
| N45 | 13.2-13.8 | -0.11 ~ -0.12 | ≥11.6 | ≥12 | -0.58 ~ -0.78 | 43-46 | 80 ℃ | 7.6 |
| N48 | 13.8-14.2 | -0.11 ~ -0.12 | ≥11.6 | ≥12 | -0.58 ~ -0.78 | 46-49 | 80 ℃ | 7.6 |
| N50 | 14.0-14.5 | -0.11 ~ -0.12 | ≥10.0 | ≥12 | -0.58 ~ -0.78 | 48-51 | 80 ℃ | 7.6 |
| N52 | 14.3-14.8 | -0.11 ~ -0.12 | ≥10.0 | ≥12 | -0.58 ~ -0.78 | 50-53 | 80 ℃ | 7.6 |
| N33M | 11.3-11.7 | -0.11 ~ -0.12 | ≥10.5 | ≥14 | -0,58 ~ -0,72 | 31-33 | 100 ℃ | 7.6 |
| N35M | 11.7-12.2 | -0.11 ~ -0.12 | ≥10.9 | ≥14 | -0,58 ~ -0,72 | 33-36 | 100 ℃ | 7.6 |
| N38M | 12.2-12.5 | -0.11 ~ -0.12 | ≥11.3 | ≥14 | -0,58 ~ -0,72 | 36-39 | 100 ℃ | 7.6 |
| N40M | 12.5-12.8 | -0.11 ~ -0.12 | ≥11.6 | ≥14 | -0,58 ~ -0,72 | 38-41 | 100 ℃ | 7.6 |
| N42M | 12.8-13.2 | -0.11 ~ -0.12 | ≥12,0 | ≥14 | -0,58 ~ -0,72 | 40-43 | 100 ℃ | 7.6 |
| N45M | 13.2-13.8 | -0.11 ~ -0.12 | ≥12,5 | ≥14 | -0,58 ~ -0,72 | 43-46 | 100 ℃ | 7.6 |
| N48M | 13.6-14.3 | -0.11 ~ -0.12 | ≥12.9 | ≥14 | -0,58 ~ -0,72 | 46-49 | 100 ℃ | 7.6 |
| N50M | 14.0-14.5 | -0.11 ~ -0.12 | ≥13,0 | ≥14 | -0,58 ~ -0,72 | 48-51 | 100 ℃ | 7.6 |
| N35H | 11.7-12.2 | -0.11 ~ -0.12 | ≥10.9 | ≥17 | -0,58 ~ -0,70 | 33-36 | 120 ℃ | 7.6 |
| N38H | 12.2-12.5 | -0.11 ~ -0.12 | ≥11.3 | ≥17 | -0,58 ~ -0,70 | 36-39 | 120 ℃ | 7.6 |
| N40H | 12.5-12.8 | -0.11 ~ -0.12 | ≥11.6 | ≥17 | -0,58 ~ -0,70 | 38-41 | 120 ℃ | 7.6 |
| N42H | 12.8-13.2 | -0.11 ~ -0.12 | ≥12,0 | ≥17 | -0,58 ~ -0,70 | 40-43 | 120 ℃ | 7.6 |
| N45H | 13.2-13.6 | -0.11 ~ -0.12 | ≥12.1 | ≥17 | -0,58 ~ -0,70 | 43-46 | 120 ℃ | 7.6 |
| N48H | 13.7-14.3 | -0.11 ~ -0.12 | ≥12,5 | ≥17 | -0,58 ~ -0,70 | 46-49 | 120 ℃ | 7.6 |
| N35SH | 11.7-12.2 | -0.11 ~ -0.12 | ≥11.0 | ≥20 | -0,56 ~ -0,70 | 33-36 | 150 ℃ | 7.6 |
| N38SH | 12.2-12.5 | -0.11 ~ -0.12 | ≥11.4 | ≥20 | -0,56 ~ -0,70 | 36-39 | 150 ℃ | 7.6 |
| N40SH | 12.5-12.8 | -0.11 ~ -0.12 | ≥11.8 | ≥20 | -0,56 ~ -0,70 | 38-41 | 150 ℃ | 7.6 |
| N42SH | 12.8-13.2 | -0.11 ~ -0.12 | ≥12.4 | ≥20 | -0,56 ~ -0,70 | 40-43 | 150 ℃ | 7.6 |
| N45SH | 13.2-13.8 | -0.11 ~ -0.12 | ≥12.6 | ≥20 | -0,56 ~ -0,70 | 43-46 | 150 ℃ | 7.6 |
| N28UH | 10.2-10.8 | -0.11 ~ -0.12 | ≥9.6 | ≥25 | -0,52 ~ -0,70 | 26-29 | 180 ℃ | 7.6 |
| N30UH | 10.8-11.3 | -0.11 ~ -0.12 | ≥10.2 | ≥25 | -0,52 ~ -0,70 | 28-31 | 180 ℃ | 7.6 |
| N33UH | 11.3-11.7 | -0.11 ~ -0.12 | ≥10.7 | ≥25 | -0,52 ~ -0,70 | 31-34 | 180 ℃ | 7.6 |
| N35UH | 11.8-12.2 | -0.11 ~ -0.12 | ≥10.8 | ≥25 | -0,52 ~ -0,70 | 33-36 | 180 ℃ | 7.6 |
| N38UH | 12.2-12.5 | -0.11 ~ -0.12 | ≥11.0 | ≥25 | -0,52 ~ -0,70 | 36-39 | 180 ℃ | 7.6 |
| N40UH | 12.5-12.8 | -0.11 ~ -0.12 | ≥11.3 | ≥25 | -0,52 ~ -0,70 | 38-41 | 180 ℃ | 7.6 |
| N28EH | 10.4-10.9 | -0.105 ~ -0.120 | ≥9.8 | ≥30 | -0,48 ~ -0,70 | 26-29 | 200 ℃ | 7.6 |
| N30EH | 10.8-11.3 | -0.105 ~ -0.120 | ≥10.2 | ≥30 | -0,48 ~ -0,70 | 28-31 | 200 ℃ | 7.6 |
| N33EH | 11.3-11.7 | -0.105 ~ -0.120 | ≥10.5 | ≥30 | -0,48 ~ -0,70 | 31-34 | 200 ℃ | 7.6 |
| N35EH | 11.7-12.2 | -0.105 ~ -0.120 | ≥11.0 | ≥30 | -0,48 ~ -0,70 | 33-36 | 200 ℃ | 7.6 |
| N38EH | 12.2-12.5 | -0.105 ~ -0.120 | ≥11.3 | ≥30 | -0,48 ~ -0,70 | 36-39 | 200 ℃ | 7.6 |
| N28AH | 10.4-10.9 | -0.105 ~ -0.120 | ≥9.9 | ≥33 | -0.45 ~ -0.70 | 26-29 | 230 ℃ | 7.6 |
| N30AH | 10.8-11.3 | -0.105 ~ -0.120 | ≥10.3 | ≥33 | -0.45 ~ -0.70 | 28-31 | 230 ℃ | 7.6 |
| N33AH | 11.3-11.7 | -0.105 ~ -0.120 | ≥10.6 | ≥33 | -0.45 ~ -0.70 | 31-34 | 230 ℃ | 7.6 |
| Noto: · Sub labora temperaturo 20 ℃ ± 2 ℃, super magnetaj parametroj kaj fizikaj ecoj estas provitaj, kun neevitebla perdo de magneta forto ne pli ol 5%. · La maksimuma labora temperaturo de magneto ŝanĝiĝas pro rilato de longo kaj diametro kaj ĉirkaŭaj faktoroj. . |
||||||||
Avantaĝo:
La ecoj de ĉi tiuj magnetoj multe superas la tradiciajn kaj ili estas nuntempe la plej potencaj en apliko. Ilia alta
trudemo kaj alta restado permesas la novan projekton kaj la eblon pliigi aplikan kampon, kie la spaco estas limigita
aŭ kie forta magneta kampo postulis.
NdFeB-magnetoj estas tre sentemaj al korodo. Tial postulu protektan surfacan tegon. Uzoj de NdFeB-magneto estas kondiĉigitaj
laŭ la temperaturo en vasta gamo de 80ºC ĝis 230ºC. Kaj ankaŭ ĝi funkcias ĉe temperaturo sub 0 ℃.
Apliko:
Neodimaj magnetoj estas uzataj kiel diversaj specoj de magnetaj lensoj por fokuso, deklino de ŝarĝitaj partikloj en elektroniko, bremsaj sistemoj,
gutado, sensilo, magneta sistemo en rotoraj kaj mikromotoroj, kaj scienca kampo, medicino (tomografio, NMR-spektrometroj), ktp.
Hodiaŭ magnetoj NdFeB estas uzataj en grandaj kvantoj tra la tuta mondo. La disvolviĝo de ĉi tiu materialo ankoraŭ ne finiĝis; la remanenco
kaj truda kampoforto estas kontinue pliigita. La alta energio de NdFeB-magnetoj signifas, ke motoroj kaj sensiloj povas esti konstruitaj
ĉiam pli malgranda - kaj ĉi tio signifas pliigon de efikeco. La daŭraj plibonigoj ebligas, ke ĉi tiu interesa materialo estu konti-
ĉiujare enkondukitaj en novajn areojn.
Ĉiuj deklaritaj valoroj estis determinitaj per normaj specimenoj laŭ IEC 60404-5. La jenaj specifoj funkcias kiel referencaj valoroj kaj
povas malsami. Por pliaj informoj bonvolu kontakti niajn inĝenierojn pri aplikaĵoj.